Ebalta MG 426 / Comp. A+B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | it9GwE_Ebalta-MG-426-Comp-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta MG 426 is processed on a two-component low pressure device. After grinding with a sand paper , grit 280, the surface can be varnished with a commercial lacquer. For better adhesion we recommend the use of a primer coat. Nitrocellulose lacquers have a better adhesion on polyurethane surfaces than on acryl-lacquer-systems. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 78 to 82 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2090 to 2290 | MPa | ISO 178 |
| Flexural Stress | 80.0 to 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 39 to 45 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 92.0 to 98.0 | °C | ISO 75-2/B |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 89 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Post Cure Time (60°C) | 6.0 to 8.0 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.15 to 1.19 | g/cm³ | |
| Viscosity (25°C) | 0.60 to 0.80 | Pa·s | |
| Curing Time (20°C) | 1.5 to 2.0 | hr | |
| Pot Life (20°C) | 2.5 to 2.7 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP WPP311D | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| NuSil CF5-3521-2 | NuSil Technology | Silicone Rubber, LSR | NuSil |
| ARLEN™ A315 | Mitsui Chemicals America, Inc. | Nylon 6T | ARLEN™ |
| Ferro PP LPP20BC02NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| LNP™ THERMOCOMP™ UF00ASW compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |