Keyflex® BT 1040D
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Keyflex® BT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | it2OLa_Keyflex-BT-1040D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose, Medium Modulus Applications Antenna Cover, Injection Parts for Leisure & Sports, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 to 1.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 92 | ||
| Shore D | 40 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 2.00 mm) | 24.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 2.00 mm) | 900 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 78.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.40 mm | No Break | ||
| 23°C, 6.40 mm | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 60.0 | °C | ASTM D648 |
| Peak Melting Temperature | 178 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| -- | > 1.0E+15 | ohms·cm | ASTM D257 |
| 23°C | > 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 1.00 mm | 26 | kV/mm | ASTM D149 |
| 23°C, 1.00 mm | 26 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (CTI) 4 | 600 | V | UL 746 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Nozzle Temperature | 200 to 220 | °C | |
| Processing (Melt) Temp | 180 to 220 | °C | |
| Mold Temperature | 10.0 to 35.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Cylinder Zone 1 Temp. | 180 to 200 | °C | |
| Cylinder Zone 2 Temp. | 190 to 210 | °C | |
| Cylinder Zone 3 Temp. | 190 to 210 | °C | |
| Cylinder Zone 4 Temp. | 190 to 210 | °C | |
| Adapter Temperature | 190 to 210 | °C | |
| Melt Temperature | 180 to 220 | °C | |
| Die Temperature | 190 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD 383 FR | RTP Company | PC | RTP |
| TEREZ PA 6 7530 GF 10 MF 20 HY | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| VINIKA® D6188 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | VINIKA® |
| Grivory® XE 4095 black 9225 | EMS-GRIVORY | Nylon 10T/X | Grivory® |
| Hostacom PPN 1034 12 | LyondellBasell Industries | PP Copolymer | Hostacom |