OnForce™ LFT LF6600-5017 Grey

Category:	Nylon 66 , Polyamide 66
Manufacturer:	PolyOne Corporation
Trademark:	OnForce™ LFT
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	isoBXo_OnForce-LFT-LF6600-5017-Grey.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Polyvan's long fiber thermoplastic polymers are used in situations where high hardness and good impact resistance are required, such as metal substitution or other structural applications. These products exhibit enhanced physical and mechanical properties compared to staple fiber products. Its advantages include improved impact strength, elasticity and material strength in different temperature ranges. In addition, compared with traditional high-filled short fiber products, long fiber thermoplastic polymers show improved properties in terms of creep and fatigue resistance, improved dimensional stability and unique surface finish.

General Information
Filler / Reinforcement	Long glass fiber
Appearance	Grey
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	1.56	g/cm³	ISO 1183

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	16700	MPa	ISO 527-2
Tensile Stress (Break)	226	MPa	ISO 527-2
Tensile Strain (Break)	1.8	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Dart Drop Impact	110	J	ASTM D3029

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	4.0	hr
Processing (Melt) Temp	290 - 320	°C
Mold Temperature	90.0	°C
Injection Rate	Slow-Moderate
Back Pressure	5.00	MPa

Injection instructions
LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.

Injection instructions

LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.

Resin Grade	Manufacturer	Category	Trademark
Tritheva® TN 2020	Petroquimica Triunfo	EVA	Tritheva®
Vyncolit® FS-6 CAF	Vyncolit N.V.	DAP	Vyncolit®
Adsyl 7423 XCP	LyondellBasell Industries	Polyolefin, Unspecified	Adsyl
Fainplast PVC FKT 0296/1	Fainplast Compounds S.r.l	PVC, Unspecified	Fainplast PVC
EMERGE™ PC 8830-5 LT	Trinseo	PC	EMERGE™