Hylex® P1032L1
| Category: | PC , Polycarbonate |
| Manufacturer: | Entec Polymers |
| Trademark: | Hylex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iseOpG_HylexP1032L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYCARBONATE, HIGH MELT FLOW, CLEAR EDGE TINT |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 32 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 66.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 130 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2250 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 750 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 130 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | V-2 | UL 94 | |
| 3.0 mm | V-2 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® A3 GF30 | A. Schulman Inc. | PBT+ASA | SCHULADUR® |
| Hyundai EP PA66 LD381* | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| K-vinyl 60 Deg C Rating Insulation (80-Wet) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| LNP™ THERMOCOMP™ UFW49S compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |
| NEOFLON™ EP-620 | DAIKIN AMERICA, INC. | ETFE | NEOFLON™ |