Reny® 1012H
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iruYdR_Reny-1012H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Reny® 1012H is a Polyarylamide (PARA) material filled with 40% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® 1012H: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.56 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 22 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 15.1 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.42 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.18 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.2 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16600 | 13600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 218 | 177 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.8 | 1.8 | % | ISO 527-2 |
| Flexural Modulus | 14900 | 13800 | MPa | ISO 178 |
| Flexural Stress | 349 | 306 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.5 | 8.9 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 52 | 52 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 237 | 232 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 226 | 218 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 5.0E-5 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 275 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Surlyn® 1901 | DuPont Packaging & Industrial Polymers | Ionomer | Surlyn® |
| NORYL PPX™ PPX7115F resin | SABIC Innovative Plastics | PPE+PS+PP | NORYL PPX™ |
| AIE PET 40G3 | Asia International Enterprise (Hong Kong) Limited | PET | AIE PET |
| LNP™ THERMOCOMP™ UF0067W compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |
| Rotuba CAB B9424 (3% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |