Clyrell RC215M
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Clyrell |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | irZExG_Clyrell-RC215M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
"Clyrell" RC215M is a alpha olefin modified polypropylene random copolymer especially designed for cast film technology. It offers an excellent clarity and gloss, a very low haze, a wide hot tack range and a low seal-initiation temperature of 120°C. It is designed for quality packaging applications, either as monolayer film or as welding layer in coextruded structures. "Clyrell" RC215M is easy processable on commercial cast film equipment. It contains slip and antiblock additives. "Clyrell" RC215M is suitable for food contact. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 66 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1050 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 27.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 10 | % | |
| Break | 600 | % | |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Cast Film | 0.50 | ||
| vs. Itself - Static, Cast Film | 0.50 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus - MD 1(50 µm, Cast Film) | 660 | MPa | ASTM D882 |
| Tensile Strength - MD 2 | ASTM D882 | ||
| Yield, 50 µm, Cast Film | 22.0 | MPa | |
| Break, 50 µm, Cast Film | 35.0 | MPa | |
| Tensile Elongation - MD 3(Break, 50 µm, Cast Film) | 750 | % | ASTM D882 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 1.5 | kJ/m² | |
| 23°C | 3.4 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 65.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 130 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (50.0 µm, Cast Film) | 90 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | < 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 25 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-737 A03 | CHI MEI CORPORATION | ABS | POLYLAC® |
| Daelim Po1y® HX-250BL | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Elastollan® 1195A55 | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| Lanufene HDI-6507N | Ras Lanuf Oil & Gas Processing Company (RASCO) | HDPE | Lanufene |
| OMIKRON KM 508 NERO | TECNOPOL | PP Homopolymer | OMIKRON |