NEXUS PC PC731
| Category: | PC , Polycarbonate |
| Manufacturer: | Nexus Resin Group, LLC. |
| Trademark: | NEXUS PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | irVL8Y_NEXUS-PC-PC731.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Molding Grade PC |
| General Information | |
|---|---|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2410 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 62.1 | MPa | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 800 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 129 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.57 mm) | HB V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 288 to 316 | °C | |
| Middle Temperature | 302 to 329 | °C | |
| Front Temperature | 316 to 343 | °C | |
| Nozzle Temperature | 316 to 343 | °C | |
| Processing (Melt) Temp | 316 to 343 | °C | |
| Mold Temperature | 79.4 to 107 | °C | |
| Back Pressure | 0.345 to 1.38 | MPa | |
| Screw Speed | 40 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrathane™ ALC-80A-B30 | Biomerics, LLC | TPU-PC | Quadrathane™ |
| Rhelon F1725H-01 | RheTech, Inc. | Nylon 6 | Rhelon |
| VESTODUR® 3000 Series | Evonik Industries AG | PBT | VESTODUR® |
| NILENE® P K30T | Taro Plast S.p.A. | PP Homopolymer | NILENE® |
| Ferro PP LPP40YR05HB | Ferro Corporation | PP Homopolymer | Ferro PP |