Tritan™ TX2001
| Category: | Copolyester , Copolyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Tritan™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | irRECO_Tritan-TX2001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Eastman Tritan™ TX2001 is an amorphous copolyester with excellent appearance and clarity. Tritan™ TX2001 contains a mold release derived from vegetable based sources. Its most outstanding features are excellent toughness, hydrolytic stability, and heat and chemical resistance. This new-generation copolyester can also be molded into various applications without incorporating high levels of residual stress. Combined with Tritan™ copolyester's outstanding chemical resistance and hydrolytic stability, these features give molded products enhanced durability in the dishwasher environment, which can expose products to high heat, humidity, and aggressive cleaning agents. Tritan™ TX2001 copolyester may be used in repeated use food contact articles under United States Food and Drug Administration (FDA) regulations. Tritan™ TX2001 copolyester is certified to NSF/ANSI Standard 51 for Food Equipment Materials and is also certified to NSF/ANSI Standard 61 - Drinking Water System Components-Health Effects. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1590 | MPa | ASTM D638 |
| 23°C | 1620 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 44.0 | MPa | ASTM D638 |
| Yield, 23°C | 45.0 | MPa | ISO 527-2 |
| Break, 23°C | 53.0 | MPa | ASTM D638 |
| Break, 23°C | 49.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 7.0 | % | ASTM D638, ISO 527-2 |
| Break, 23°C | 140 | % | ASTM D638 |
| Break, 23°C | 130 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1590 | MPa | ASTM D790 |
| 23°C | 1530 | MPa | ISO 178 |
| Flexural Strength (Yield, 23°C) | 66.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 650 | J/m | ASTM D256 |
| -40°C | 14 | kJ/m² | ISO 180 |
| 23°C | 66 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 109 | °C | |
| 1.8 MPa, Unannealed | 92.0 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Total) | 92.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 88.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 282 | °C | |
| Mold Temperature | 38.0 to 66.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LAF419 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| SOLPLAST TH 9000D | UTEKSOL d.o.o. | SBS | SOLPLAST TH |
| Sup-tech H706 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 46 | Sup-tech |
| KOPLA PA66 KDG1133CR | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| Sylvin 9915-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |