High Density Polyethylene Copolymer Extrusion - Blow Molding

Applications

KPOL - HD K-0.75/952 is specially formulated for the production of stretched tapes, monofilament and blown film.

Characterisitics

KPOL - HD K-0.75/952 is a medium molecular weight extrusion grade of high density polyethylene. If this product is used for food contact applications, then the user needs to ensure compliance with the requirements of relevant FDA regulations.

General Information
Additive	Antioxidant (300 to 600 ppm)
Features	Antioxidant Copolymer Food Contact Acceptable High Density Medium Molecular Weight
Uses	Blown Film Monofilaments Tape
Forms	Pellets
Processing Method	Blown Film Extrusion Extrusion Blow Molding Film Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.952	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.75	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance ¹
50°C, 3.18 mm, 100% Igepal CO-630, F50	15.0 to 20.0	hr	ASTM D1693A
50°C, 1.91 mm, 100% Igepal CO-630, F50	8.00 to 10.0	hr	ASTM D1693B

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 1 sec, 23°C)	65		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ²(Yield)	30.3	MPa	ASTM D638
Tensile Elongation ³(Break)	> 300	%	ASTM D638
Flexural Modulus - Tangent ⁴(3.20 mm)	1650	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Tensile Impact Strength	126	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	79.0	°C	ASTM D648
Brittleness Temperature ⁵	< -76.0	°C	ASTM D746A
Vicat Softening Temperature	130	°C	ASTM D1525 ⁶

Note Message
1 .	Grooved Specimen
2 .	Type IV, 50 mm/min
3 .	Type IV, 50 mm/min
4 .	13 mm/min
5 .	F50; 25 lbfXin
6 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
PureTherm® 3007C Opaque	Tekni-Films, a div of Tekni-Plex	Film, PVC	PureTherm®
Thermec™ 4150R50	Technical Polymers, LLC	PPS	Thermec™
Dryflex® 600350S	ELASTO	SEBS	Dryflex®
Laprene® 830000951	SO.F.TER. SPA	SEBS	Laprene®
Iupital® LO-21A	Mitsubishi Engineering-Plastics Corp	Acetal (POM) Copolymer	Iupital®