Jamplast Inj-02C ABS
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ir49TP_Jamplast-Inj-02C-ABS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jamplast Inj-02C ABS is a clear general-purpose injection molding grade of ABS (Acrylonitrile Butadiene Styrene). Typical applications include housings, toys, small appliances, and consumer goods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 20 | g/10 min | |
| Molding Shrinkage - Flow | 0.30 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 3.17 mm) | 44.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.17 mm) | > 50 | % | ASTM D638 |
| Flexural Modulus (3.17 mm) | 2140 | MPa | ASTM D790 |
| Flexural Strength (Yield, 3.17 mm) | 66.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 3.17 mm | 120 | J/m | |
| 6.35 mm | 96 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 93.0 | °C | ISO 306 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Transmittance (3000 µm) | 90.0 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 68.5 to 108 | MPa | |
| Back Pressure | 0.979 to 1.96 | MPa | |
| Screw Speed | 60 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Celanex® 5205HG | Celanese Corporation | PBT | Celanex® |
| Karina IVORY PVC COMPOUND 450-35/1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| RTP 199 X 143684 B | RTP Company | PP, Unspecified | RTP |
| Sylvin 8354-62D Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| EPAMOULD 795A15 | Epaflex Polyurethanes S.R.L. | TPU-Polyether | EPAMOULD |