Udel® P-3700 HC
| Category: | PSU , Polysulfone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Udel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iq0eVS_Udel-P-3700-HC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Udel® P-3700 HC is a high-clarity grade of polysulfone (PSU) that is nearly water-white in color. This grade was designed to eliminate the yellow cast and provide design flexibility and improved aesthetics for applications where a yellow cast is undesirable. Compared to Udel® P-1700, P-3700 HC has higher flow and a slightly greater tendency to stress crack in some aggressive environments. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (343°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2690 | MPa | ASTM D638 |
| Tensile Strength | 75.8 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.8 | % | ASTM D638 |
| Fracture | 45 | % | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, 3.18 mm) | 178 | °C | ASTM D648 |
| Glass Transition Temperature | 185 | °C | ASTM E1356 |
| CLTE - Flow | 5.6E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.635 | ASTM D542 | |
| Transmittance (2540 µm) | 77.0 - 83.0 | % | ASTM D1003 |
| Haze (2540 µm) | 2.0 | % | ASTM D1003 |
| Yellowness Index (2.54 mm) | 2.0 | YI | ASTM D1925 |
| Additional Information |
|---|
| Tensile Elongation at Break, ASTM D638: 30 to 60 % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 3.0 | hr | |
| Drying Time, Maximum | 3.5 | hr | |
| Suggested Shot Size | 50 - 75 | % | |
| Hopper Temperature | 149 | °C | |
| Processing (Melt) Temp | 329 - 385 | °C | |
| Mold Temperature | 121 - 163 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermoset Plastics 351 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Bapolene® 3262 | Bamberger Polymers, Inc. | HDPE | Bapolene® |
| DuraMax™ DMX 8070NC | Advanced Polymer Alloys | TPE | DuraMax™ |
| K-vinyl 70 Deg C Rating Insulation (85-Dry) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| Karina BLACK PVC COMPOUND 807D48/1-D-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |