HK HIPS SRG100
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Hong Kong Petrochemical Co. Ltd. |
| Trademark: | HK HIPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iplWva_HK-HIPS-SRG100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HK HIPS SRG100 is a High Impact Polystyrene material. It is available in Asia Pacific. Important attributes of HK HIPS SRG100 are:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Apparent Density | 0.65 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 72 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 2000 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 3.20 mm | 30.0 | MPa | |
| 3.20 mm | 23.0 | MPa | |
| Tensile Elongation 3(Break, 3.20 mm) | 58 | % | ASTM D638 |
| Flexural Modulus (3.20 mm) | 2100 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm) | 52.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 90.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 103 | °C | ASTM D1525 4 |
| -- | 96.0 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 98 | ASTM D523 |
| Note Message | |
|---|---|
| 1 . | Type I |
| 2 . | Type I |
| 3 . | Type I |
| 4 . | Rate A (50°C/h), Loading 1 (10 N) |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polypropylene C7020-20 ESU CZ175 | Trinseo | PP, Unspecified | Polypropylene |
| SILVER® ABS 350C | Guangdong Silver Age Sci & Tech. Co., Ltd | ABS+PVC | SILVER® |
| TEKANATE™ G7007 | Mando Advanced Materials Co., Ltd. | PC | TEKANATE™ |
| Zythane® 4065A | Alliance Polymers & Services | TPU-Polyester | Zythane® |
| I. Stern 3335 | I. STERN & CO. INC. | PP Impact Copolymer | I. Stern |