K-Prene TPE LSZH 70
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Technovinyl Polymers India Ltd. |
| Trademark: | K-Prene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iouRGo_K-Prene-TPE-LSZH-70.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
K-Prene TPE LSZH 70 is a Thermoplastic Elastomer (TPE) material. It is available in Africa & Middle East. Important attributes of K-Prene TPE LSZH 70 are:
Typical application of K-Prene TPE LSZH 70: Wire & Cable |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 to 1.38 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (160°C/21.6 kg) | 3.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 65 to 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus - 2% Secant | 100 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 2.94 to 4.90 | MPa | ASTM D412 |
| Tensile Elongation 2(Break) | 350 to 450 | % | ASTM D412 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (100°C, 168 hr) | 20 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (100°C, 168 hr) | -32 | % | ASTM D573 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -20.0 | °C | ASTM D746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 29 | % | ASTM D2863 |
| Heat Release | ASTM E1354 | ||
| Average | 84 | kW/m² | |
| Peak | 128 | kW/m² |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Knife Test (90°C) 3 | Passes | IEC 540 | |
| Specific Energy - Average | 216000 | m²/kg | ASTM E1354 |
| Time to Ignition | 2.8 | min | ASTM E1354 |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 4 hrs, % penetration, Clause 8 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP R7701 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Moplen EP300N | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| APICAL 200AV | Kaneka Corporation | PI, TS | APICAL |
| LEXAN™ PC1800R resin | SABIC Innovative Plastics | PC | LEXAN™ |
| OLEFISTA™ QM4301E/QCM292 | Mitsubishi Chemical Performance Polymers, Inc. | Elastomer, Specialty | OLEFISTA™ |