Starflam RF0077E
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starflam |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ioiRl3_Starflam-RF0077E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starflam RF0077E is a Halogen Free and Red Phosphorous Free Flame Retardant, Glass Fiber Reinforced, Polyamide 66 Injection Molding Resin (also known as RF1007Z270) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.70 to 1.1 | % | |
| Flow : 4.00 mm | 0.10 to 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 155 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 10400 | MPa | ISO 178 |
| Flexural Stress | 216 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 245 | °C | ISO 75-2/Af |
| Ball Pressure Test 5(240°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 110 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 775 | °C | |
| 1.50 mm | 775 | °C | |
| 3.00 mm | 825 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 265 to 275 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Processing (Melt) Temp | 270 to 280 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| McCann PP M30CHPP10 | McCann Plastics Inc. | PP Homopolymer | McCann PP |
| Sindustris PC SR3109FC | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| Niplene F15 | Soredi S.p.a. | PP Homopolymer | Niplene |
| 3M™ Dyneon™ Fluoroplastic FEP 6322HTZ | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |
| ECP 172 | TBA Electro Conductive Products Ltd. | PS (GPPS) | ECP |