EVAL™ SP434
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ioeyzw_EVAL-SP434.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Orientability Ethylene Vinyl Alcohol Copolymer Applications: PET Co-injection |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 4.4 | g/10 min | |
| 210°C/2.16 kg | 11 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 29.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 20 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Carbon Dioxide Transmission Rate | ISO 14663-2 | ||
| 20°C, 0.65% RH | 1.24 | cm³/m²/24 hr | |
| 20°C, 0.85% RH | 7.75 | cm³/m²/24 hr | |
| Oxygen Permeability | ISO 14663-2 | ||
| 20°C, 65% RH | 9.8E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 85% RH | 0.051 | cm³·mm/m²/atm/24 hr |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 55.0 | °C | ISO 11357-2 |
| Melting Temperature | 181 | °C | ISO 11357 |
| Peak Crystallization Temperature | 158 | °C | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SFC7000 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| NatureFlex™ 45NVR | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| Chemical Resources PET08012 | Chemical Resources, Inc. | PET | Chemical Resources |
| DJSilicone NE-Z250 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Karina BLACK PVC COMPOUND 809D48/1-C-AC-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |