Nylon-MXD6 K7007C
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Gas Chemical America, Inc. |
| Trademark: | Nylon-MXD6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | in7ulA_Nylon-MXD6-K7007C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon-MXD6 K7007C is a Polyarylamide (PARA) product. It is available in Asia Pacific, Europe, or North America. Typical application: Food Contact Applications. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Water Absorption (Equilibrium, 20°C, 65) | 5.8 | % | ASTM D570 |
| Moisture Regain 1(20°C) | 3.1 | % | ASTM D570 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Distortion | 96 | °C | ASTM D648 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Semi-Crystallization Time (160°C) | 1.5 | min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4700 | MPa | ASTM D638 |
| Tensile Strength | 99.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus | 4400 | MPa | ASTM D790 |
| Flexural Strength | 160 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Carbon Dioxide Transmission Rate (23°C, 60% RH) | 0.420 | cm³/m²/24 hr | |
| Oxygen Permeability | |||
| 23°C 2 | 0.110 | cm³/m²/24 hr | |
| 23°C 3 | 0.0700 | cm³/m²/24 hr | |
| Water Vapor Transmission Rate (40°C, 90% RH) | 1.4 | g/m²/24 hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 20 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 85.0 | °C | DSC |
| Melting Temperature | 237 | °C | DSC |
| CLTE - Flow | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | Equilibrium, 65% relative humidity |
| 2 . | 80%RH |
| 3 . | 60%RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axiall PVC 19855 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Celstran® PBT-GF50-08 | Celanese Corporation | PBT | Celstran® |
| Huafon JF-W-BK3045 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| PETOPLEN MH 418 | PETKIM Petrokimya Holding A.S. | PP, Unspecified | PETOPLEN |
| SCHULAFORM® 9D DB LE BLACK | A. Schulman Europe | Acetal (POM) Copolymer | SCHULAFORM® |