AvaSpire® AV-651 is an unreinforced polyaryletherketone (PAEK) that offers more ductility and impact strength than PEEK, with higher chemical and environmental stress cracking resistance than AvaSpire® AV-650. It has been specifically formulated for applications requiring a balance of chemical resistance and mechanical strength along with good part aesthetics, bridging the performance gaps within the ultra polymers space.

These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses.

AvaSpire® AV-651 can be easily processed by typical injection molding and extrusion methods using conventional processing equipment.

Natural: AvaSpire AV-651 NT

Beige: AvaSpire AV-651 BG 15

General Information
Features	Autoclave Sterilizable Biocompatible Ductile E-beam Sterilizable Ethylene Oxide Sterilizable Fatigue Resistant Flame Retardant Good Chemical Resistance Good Dimensional Stability Good Impact Resistance Good Sterilizability Heat Sterilizable High Heat Resistance Radiation (Gamma) Resistant Radiation Sterilizable Radiotranslucent Steam Resistant Steam Sterilizable
Uses	Aerospace Applications Aircraft Applications Bearings Dental Applications Film Hospital Goods Industrial Applications Medical Devices Medical/Healthcare Applications Oil/Gas Applications Pump Parts Seals Surgical Instruments
Agency Ratings	FAA FAR 25.853a 3 ISO 10993 ISO 10993-Part 1
RoHS Compliance	RoHS Compliant
Appearance	Beige Natural Color
Forms	Pellets
Processing Method	Extrusion Blow Molding Fiber (Spinning) Extrusion Film Extrusion Injection Blow Molding Injection Molding Machining Profile Extrusion Thermoforming Wire & Cable Extrusion
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.29	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (400°C/2.16 kg)	25	g/10 min	ASTM D1238
Molding Shrinkage ¹			ASTM D955
Flow : 3.18 mm	0.70 to 0.90	%
Across Flow : 3.18 mm	1.0 to 1.2	%
Water Absorption (24 hr)	0.20	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	94		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
-- ²	3000	MPa	ASTM D638
--	3200	MPa	ISO 527-2/1A/1
Tensile Stress
Yield	89.0	MPa	ISO 527-2/1A/50
-- ³	87.0	MPa	ASTM D638
Tensile Elongation
Yield ⁴	6.2	%	ASTM D638
Yield	5.7	%	ISO 527-2/1A/50
Break ⁵	> 40	%	ASTM D638
Break	> 40	%	ISO 527-2/1A/50
Flexural Modulus
--	3100	MPa	ASTM D790
--	3200	MPa	ISO 178
Flexural Strength
--	124	MPa	ASTM D790
--	127	MPa	ISO 178
Compressive Strength	112	MPa	ASTM D695
Shear Strength	78.0	MPa	ASTM D732

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact
--	69	J/m	ASTM D256
--	6.6	kJ/m²	ISO 180
Unnotched Izod Impact	No Break		ASTM D256, ISO 180

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load ⁶(1.8 MPa, Annealed, 3.20 mm)	190	°C	ASTM D648
Glass Transition Temperature	158	°C	ASTM D3418
Peak Melting Temperature	345	°C	ASTM D3418
CLTE - Flow (-50 to 50°C)	4.7E-5	cm/cm/°C	ASTM E831
Specific Heat			DSC
50°C	1310	J/kg/°C
200°C	1820	J/kg/°C
Thermal Conductivity	0.24	W/m/K	ASTM E1530

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.9E+17	ohms	ASTM D257
Volume Resistivity	5.0E+17	ohms·cm	ASTM D257
Dielectric Strength (3.00 mm)	16	kV/mm	ASTM D149
Dielectric Constant			ASTM D150
60 Hz	3.10
1 kHz	3.12
1 MHz	3.10
Dissipation Factor			ASTM D150
60 Hz	1.0E-3
1 kHz	1.0E-3
1 MHz	4.0E-3

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.800 mm	V-0
1.60 mm	V-0

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (400°C, 1000 sec^-1)	240	Pa·s	ASTM D3835

Injection	Nominal Value	Unit
Drying Temperature	150	°C
Drying Time	4.0	hr
Rear Temperature	355	°C
Middle Temperature	365	°C
Front Temperature	370	°C
Nozzle Temperature	375	°C
Processing (Melt) Temp	365 to 390	°C
Mold Temperature	150 to 180	°C
Injection Rate	Fast
Screw Compression Ratio	2.0:1.0 to 3.0:1.0

Note Message
1 .	5" x 0.5" x 0.125"
2 .	50 mm/min
3 .	50 mm/min
4 .	50 mm/min
5 .	50 mm/min
6 .	2 hours at 200°C

Resin Grade	Manufacturer	Category	Trademark
Versaflex™ OM 6275-1	PolyOne Corporation	TPE	Versaflex™
TOTAL Polystyrene Crystal CX5197	TOTAL Refining & Chemicals	PS (GPPS)	TOTAL Polystyrene
LightSpan® LS-3252	NuSil Technology	Silicone	LightSpan®
Sylvin 8250-90 White 1570	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
FINGERPRINT™ DFDD-7525 NT	The Dow Chemical Company	MDPE	FINGERPRINT™