Polytron® P30N07
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | Polytron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | imHEte_Polytron-P30N07.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A chemically coupled 30% LGF reinforced natural PP, heat stabilized, UV stabilized for injection moulding applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.20 to 0.40 | % | |
| -- | 0.20 to 0.40 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 115 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 6500 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 170 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 17 | kJ/m² | |
| 23°C | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 50 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | 190 | J/m | ASTM D256 |
| 23°C | 19 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 149 | °C | ASTM D648, ISO 75-2/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Glow Wire Flammability Index | 750 | °C | IEC 60695-2-12 |
| Flammability (2.00 mm) | 30 | mm/min | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTOLIT® P 1982 K | VESTOLIT GmbH & Co. KG | PVC Copolymer | VESTOLIT® |
| XYRON™ 240W | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Dynaflex™ G7670-9 (Black) | PolyOne Corporation | TPE | Dynaflex™ |
| HOPELEX PCN-2002 | Lotte Chemical Corporation | PC | HOPELEX |
| Romiloy® 3020/01-4 M10 | ROMIRA GmbH | ASA+Nylon | Romiloy® |