AZDEL™ U421-B01 (Transverse)

Category:	PP Alloy , Polypropylene Alloy
Manufacturer:	Azdel, Inc.
Trademark:	AZDEL™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ilGXki_AZDEL-U421-B01-Transverse-.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
AZDEL™U421-B01 (Transverse) is a polypropylene alloy (PP alloy) material,. This product is available in North America,.

General Information
Appearance	Black
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage - Flow	0.10 - 0.30	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	5310	MPa	ISO 527-2
Tensile Stress (Yield)	60.0	MPa	ISO 527-2
Tensile Strain (Break)	2.3	%	ISO 527-2
Flexural Modulus	4800	MPa	ISO 178
Flexural Stress	145	MPa	ISO 178

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	143	°C	ASTM D648

Flammability	Nominal Value	Unit	Test Method
Burning Rate	4.6	mm/min	ISO 3795

Additional Information
Filler Content by Weight, Internal Test Method, Ashing: 42%Sheet Thickness, Internal Test Method: 3.9 mmBasis Weight, Internal Test Method, Mass per unit area: 4.7 kg/m²Multi-axial Impact, ASTM D3763 Test Method, 4mm, Max Load: 700kgSpecific Gravity, ASTM D792 Test Method, Laminate: 1.21 sp gr 23/23°CSpecific Gravity, ASTM D792 Test Method, Molded: 1.21 sp gr 23/23°CCoefficient of Thermal Expansion, ASTM E831 Test Method, -40 to 120°C ( -40 to 250°F): 37 ppm/°CNotched Izod Impact Strength, ISO 180 Test Method, 23°C, 4.0mm: 720 J/mPoission's Ratio, ISO 527 Test Method: 0.361

Additional Information

Filler Content by Weight, Internal Test Method, Ashing: 42%Sheet Thickness, Internal Test Method: 3.9 mmBasis Weight, Internal Test Method, Mass per unit area: 4.7 kg/m²Multi-axial Impact, ASTM D3763 Test Method, 4mm, Max Load: 700kgSpecific Gravity, ASTM D792 Test Method, Laminate: 1.21 sp gr 23/23°CSpecific Gravity, ASTM D792 Test Method, Molded: 1.21 sp gr 23/23°CCoefficient of Thermal Expansion, ASTM E831 Test Method, -40 to 120°C ( -40 to 250°F): 37 ppm/°CNotched Izod Impact Strength, ISO 180 Test Method, 23°C, 4.0mm: 720 J/mPoission's Ratio, ISO 527 Test Method: 0.361

Resin Grade	Manufacturer	Category	Trademark
RTP 4700 TFE 10 SI 2	RTP Company	PTT	RTP
Smoothblend® POM-1400	Colour Image Plastic Compound Sdn. Bhd. (CIPC)	Acetal (POM) Homopolymer	Smoothblend®
TRIREX® 3020U(17)	Samyang Corporation	PC	TRIREX®
KOCETAL® K300LOBBN	Kolon Plastics, Inc.	Acetal (POM) Copolymer	KOCETAL®
Sylvin 8600-80UV Clear	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin