NORYL™ GFN2 resin

Category: PPE+PS , Polyphenylene Ether + PS
Manufacturer: SABIC Innovative Plastics
Trademark: NORYL™
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: iin0mu_NORYL-GFN2-resin.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
PPE+PS blend. 20% Glass reinforced. UL746C F1. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump housings and impellers, valve components and others.
General Information
Filler / Reinforcement
  • Glass Fiber, 20% Filler by Weight
Features
  • Good Dimensional Stability
  • Hydrolytically Stable
  • Low to No Water Absorption
Agency Ratings
  • FDA Unspecified Rating
  • NSF 61
Processing Method
  • Injection Molding
Multi-Point Data
  • Coefficient of Thermal Expansion vs. Temperature (ASTM E831)
  • Elastic Modulus vs Temperature (ASTM D4065)
  • Flexural DMA (ASTM D4065)
  • Instrumented Impact (Energy) (ASTM D3763)
  • Instrumented Impact (Load) (ASTM D3763)
  • Pressure-Volume-Temperature (PVT - Zoller Method)
  • Shear DMA (ASTM D4065)
  • Specific Heat vs. Temperature (ASTM D3417)
  • Tensile Creep (ASTM D2990)
  • Tensile Fatigue
  • Tensile Stress vs. Strain (ASTM D638)
  • Thermal Conductivity vs. Temperature (ASTM E1530)
  • Viscosity vs. Shear Rate (ASTM D3835)
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.20g/cm³ASTM D792
Melt Mass-Flow Rate (MFR) (300°C/5.0 kg)9.0g/10 minASTM D1238
Melt Volume-Flow Rate (MVR) (300°C/5.0 kg)8.10cm³/10minISO 1133
Molding Shrinkage - Flow (3.20 mm)0.20 to 0.50%Internal Method
Water Absorption (24 hr)0.060%ASTM D570
Outdoor Suitability f1UL 746C
HardnessNominal ValueUnitTest Method
Rockwell Hardness (L-Scale)106ASTM D785
MechanicalNominal ValueUnitTest Method
Tensile Modulus
    -- 16200MPaASTM D638
    -- 7070MPaISO 527-2/1
Tensile Strength
    Break 290.0MPaASTM D638
    Break 97.3MPaISO 527-2/5
Tensile Elongation
    Break 32.6%ASTM D638
    Break 2.5%ISO 527-2/5
Flexural Modulus
    50.0 mm Span 45800MPaASTM D790
    -- 56540MPaISO 178
Flexural Stress
    -- 167MPaISO 178
    Yield, 50.0 mm Span 6160MPaASTM D790
ImpactNominal ValueUnitTest Method
Charpy Notched Impact Strength (23°C)12kJ/m²ISO 179/2C
Notched Izod Impact
    -40°C 96J/mASTM D256
    23°C 120J/mASTM D256
    23°C 711kJ/m²ISO 180/1A
Unnotched Izod Impact (23°C)650J/mASTM D4812
Instrumented Dart Impact (23°C, Total Energy)22.6JASTM D3763
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load
    0.45 MPa, Unannealed, 3.20 mm 141°CASTM D648
    0.45 MPa, Unannealed, 6.40 mm 143°CASTM D648
    0.45 MPa, Unannealed, 100 mm Span 8143°CISO 75-2/Be
    1.8 MPa, Unannealed, 3.20 mm 135°CASTM D648
    1.8 MPa, Unannealed, 6.40 mm 138°CASTM D648
    1.8 MPa, Unannealed, 100 mm Span 9137°CISO 75-2/Ae
Vicat Softening Temperature
    -- 143°CISO 306/B50
    -- 146°CISO 306/B120
CLTE ASTM E831
    Flow : -40 to 40°C 2.9E-5cm/cm/°C
    Transverse : -40 to 40°C 8.3E-5cm/cm/°C
RTI Elec 90.0°CUL 746
RTI Imp 90.0°CUL 746
RTI Str 90.0°CUL 746
ElectricalNominal ValueUnitTest Method
Dielectric Strength (3.20 mm, in Oil)17kV/mmASTM D149
Dielectric Constant ASTM D150
    50 Hz 2.86
    60 Hz 2.86
Dissipation Factor ASTM D150
    50 Hz 8.0E-4
    60 Hz 8.0E-4
Arc Resistance 10PLC 7ASTM D495
High Amp Arc Ignition (HAI) PLC 4UL 746
High Voltage Arc Tracking Rate (HVTR) PLC 4UL 746
Hot-wire Ignition (HWI) PLC 4UL 746
FlammabilityNominal ValueUnitTest Method
Flame Rating (1.47 mm)HBUL 94
Oxygen Index 26%ASTM D2863
InjectionNominal ValueUnit
Drying Temperature 110 to 121°C
Drying Time 3.0 to 4.0hr
Drying Time, Maximum 8.0hr
Suggested Max Moisture 0.020%
Suggested Shot Size 30 to 70%
Rear Temperature 266 to 316°C
Middle Temperature 277 to 321°C
Front Temperature 288 to 327°C
Nozzle Temperature 299 to 327°C
Processing (Melt) Temp 299 to 327°C
Mold Temperature 82.2 to 110°C
Back Pressure 0.345 to 0.689MPa
Screw Speed 20 to 100rpm
Note Message
1 .5.0 mm/min
2 .Type I, 5.0 mm/min
3 .Type I, 5.0 mm/min
4 .1.3 mm/min
5 .2.0 mm/min
6 .1.3 mm/min
7 .80*10*4
8 .120*10*4 mm
9 .120*10*4 mm
10 .Tungsten Electrode
Resin Grade Manufacturer Category Trademark
Witcom POM-C 2008/325 Blue Witcom Engineering Plastics B.V. Acetal (POM) Copolymer Witcom POM-C
Arlon® 44N Arlon-MED Epoxy Arlon®
Generic PETG Generic PETG Generic
Laramid G/45 LATI S.p.A. PPA Laramid
PPO™ 646 resin SABIC Innovative Plastics PPE+PS PPO™