Ecomann® PHA EM10000
| Category: | PHA , Polyhydroxyalkanoate |
| Manufacturer: | Shenzhen Ecomann Biotechnology Co., Ltd. |
| Trademark: | Ecomann® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ihpw2Y_Ecomann-PHA-EM10000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EM10000 is semi-crystalline biodegradable, aliphatic bio-polyester designed for use in film applications. EM10000 is certificated to meet EU direct food contact, EN13432 and OK Home compost standards for biodegradable plastics. Typical applications: Blown and cast film applications, such as paper coating |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (170°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Water Absorption (Equilibrium) | < 0.40 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 13.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 550 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Transmission Rate (40°C, 90% RH, 70 µm) | 160 | cm³/m²/24 hr | |
| Water Vapor Transmission Rate (25°C, 90% RH, 70 µm) | 13 | g/m²/24 hr |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 1 |
| Melting Temperature | 120 to 140 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index | 60 | YI | Internal Method |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blow Molding Barrel Temperature | |||
| Compression Section | 110 to 125 | °C | |
| Feed Temperature | 100 to 115 | °C | |
| Melting Section | 110 to 125 | °C | |
| Blow Molding Die Temperature | 120 to 135 | °C | |
| Blow Molding Melt Temperature | 120 to 140 | °C | |
| Blow Molding Screw Speed | 30 to 50 | rpm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Extruder Screw L/D Ratio | 20.0:1.0 to 30.0:1.0 | ||
| Extruder Screw Compression Ratio | 1.5:1.0 to 3.0:1.0 | ||
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Advanced Composites ADX-5023 | Advanced Composites, Inc. | TPO | Advanced Composites |
| EVAL™ F104B | EVAL Europe nv | EVOH | EVAL™ |
| Hostacom PP 3100 10 | LyondellBasell Industries | PP Copolymer | Hostacom |
| POLYfill PPH TS15010 H VTUV1 | Polykemi AB | PP Homopolymer | POLYfill |
| Bapolene® 108A | Bamberger Polymers, Inc. | LDPE | Bapolene® |