LNP™ LUBRICOMP™ YL003 compound
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ihkP1n_LNP-LUBRICOMP-YL003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* YL003 is a compound based on Polyester Elastomer resin containing 15% PTFE. Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound YL-4030 Product reorder name: YL003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.28 | g/cm³ | |
| -- | 1.27 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.33 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.47 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 237 | MPa | ASTM D638 |
| -- | 249 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 43.0 | MPa | ASTM D638 |
| Yield | 14.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 3 | 14 | % | ASTM D638 |
| Yield | 44 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 237 | MPa | ASTM D790 |
| -- 5 | 228 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 310 | J/m | ASTM D256 |
| 23°C 6 | 36 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 460 | J/m | ASTM D4812 |
| 23°C 7 | 43 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 25.6 | J | ASTM D3763 |
| -- | 24.3 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.7E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.9E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 204 to 216 | °C | |
| Front Temperature | 227 to 238 | °C | |
| Processing (Melt) Temp | 216 to 238 | °C | |
| Mold Temperature | 26.7 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V962 NAT601/BLK 580 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Yanshan PE LD157 | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| Ultramid® A3X3G5 | BASF Corporation | Nylon 66 | Ultramid® |
| Braskem PP R131-02A | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| Durethan® BKV 230 H2.0 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |