EMERGE™ PC/ABS 7890
| Category: | PC+ABS , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ihO42G_EMERGEPCABS7890.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC/ABS 7890 Advanced Resin is an ignition-resistance PC/ABS alloy contains no chlorine or bromine additives. This resin provides superior processability for molding thin-wall parts and optimizing cycle time productivity in injection molding operations. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/3.8 kg | 14 | g/10 min | ASTM D1238 |
| 260°C/5.0 kg | 57 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.20 mm, Injection Molded) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2280 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.20mm, injection molding | 60.0 | MPa | ASTM D638 |
| Fracture, 3.20mm, injection molding | 46.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.20mm, injection molding | 3.2 | % | ASTM D638 |
| Fracture, 3.20mm, injection molding | 37 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2670 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 93.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 550 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 90.0 | °C | ASTM D648 |
| 0.45 MPa, annealed | 94.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 78.0 | °C | ASTM D648 |
| 1.8 MPa, annealed | 90.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 106 | °C | ASTM D1525 1 |
| -- | 94.0 | °C | ASTM D1525 2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.50 mm, all color 3 | V-2 | UL 94 | |
| 1.0 mm, all color 4 | V-1 | UL 94 | |
| 1.0 mm, NC, BK 5 | V-0 | UL 94 | |
| 1.4 mm, all color 6 | V-0 | UL 94 | |
| 1.4 mm, all color 7 | 5VB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 40 - 70 | °C |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h), 压 力1 (10N) |
| 2 . | 速率 A (50°C/h), 载荷2 (50N) |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 5 . | This rating is not intended to reflect the danger caused by this or any other material under actual fire conditions. |
| 6 . | This rating is not intended to reflect the danger caused by this or any other material under actual fire conditions. |
| 7 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimePart® PLUS PA 2221 | EOS GmbH | Nylon 12 | PrimePart® |
| THERMORUN® 3755B/N | Mitsubishi Chemical Performance Polymers, Inc. | TPE | THERMORUN® |
| Chemlon® 240 MH | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| EPOPLEN PP CFR 10 NC | EPSAN Plastik SAN. ve TiC. A.S. | PP, Unspecified | EPOPLEN |
| Hifax HSBMCB1158PC | LyondellBasell Industries | TPO (POE) | Hifax |