Durethan® DP AKV 30 HR EF 901510
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS Asia/Pacific |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iguxQK_Durethan-DP-AKV-30-HR-EF-901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 30 % glass fibers, injection molding, improved flowability, heat-aging stabilized, hydrolysis stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.32 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 290°C, 2.00 mm 1 | 0.82 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.040 | -- | % | |
| Flow : 290°C, 2.00 mm 3 | 0.37 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.060 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8200 | 5000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 150 | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.6 | 8.0 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 8100 | 5000 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | 225 | 125 | MPa | |
| 23°C 6 | 240 | 150 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 4.0 | 6.0 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Burning Behavior 8 | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66, GHRW, 14-080, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | -- | kJ/m² | |
| 23°C | 10 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | -- | kJ/m² | |
| 23°C | 80 | 80 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | 10 | 15 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 65 | 60 | kJ/m² | |
| 23°C | 70 | 70 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 2.50 | -- | J | |
| 23°C | 2.70 | -- | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 756 | -- | N | |
| 23°C | 774 | -- | N |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| Melting Temperature 9 | 263 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | US-FMVSS302 |
| 9 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LL6F 809-HSB | Marco Polo International, Inc. | LLDPE | MARPOL® |
| Cheng Yu IPS600UV | Cheng Yu Plastic Company Limited | PS (HIPS) | Cheng Yu |
| Durethan® BKV 35 H2.0 901510 | LANXESS Corporation | Nylon 6 | Durethan® |
| TECACOMP® PA66 ID blue 4067 | Ensinger GmbH | Nylon 66 | TECACOMP® |
| OnForce™ LFT AM-60LGF/001 BLACK | PolyOne Corporation | PPA | OnForce™ LFT |