SCANAMID 66 A52^E
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Polykemi AB |
| Trademark: | SCANAMID 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | igilRL_SCANAMID-66-A52-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified |
| General Information |
|---|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.08 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.8 | -- | % | |
| Flow | 1.6 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 70 | -- | ASTM D2240 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | 50.0 | 40.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | |||
| Yield | 8.0 | 40 | % | |
| Break | 55 | > 100 | % | |
| Flexural Modulus (23°C) | 2100 | 1200 | MPa | ISO 178 |
| Flexural Stress | 90.0 | 45.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -20°C | 40 | -- | kJ/m² | |
| 23°C | 60 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1 | ||||
| 0.45 MPa, Unannealed | 180 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULABLEND® (PA/PP) M/MO GF 25 | A. Schulman Europe | Nylon+PP | SCHULABLEND® |
| Sylvin 8422-70 Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| Moplen EP500M | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| COPYLENE® CM015G | Phillips 66 | PP Impact Copolymer | COPYLENE® |
| Ebalta AH 120 / TGL | Ebalta Kunststoff GmbH | Epoxy | Ebalta |