LIHAN® A7010
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nanjing Lihan Chemical Co., Ltd. |
| Trademark: | LIHAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | igKA8w_LIHAN-A7010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LIHAN®A7010 is a polyamide 66 (nylon 66) product,. It can be processed by injection molding and is available in the Asia-Pacific region. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.56 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.20 - 0.50 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.50 - 0.90 | -- | % | ISO 62 |
| Moisture Content | 4.0 - 5.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | 117 | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress (Break) | 210 | 170 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | 3.5 | % | ISO 527-2 |
| Flexural Modulus | 13000 | 11500 | MPa | ISO 178 |
| Flexural Stress | 310 | 240 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 13 | 15 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 255 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | DSC |
| CLTE - Flow | 5.0E-6 - 2.0E-5 | 5.0E-5 - 6.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | ASTM D257 |
| Dielectric Strength | 20 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.59 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 270 - 310 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PP ABS AF312C | Performance Plastics, Ltd. | ABS | PP ABS |
| Quadrant EPP CESTILENE HD 500R | Quadrant Engineering Plastic Products | HMWPE | Quadrant EPP |
| Abstron SE32 | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Daicel PP FP994 | Daicel Polymer Ltd. | PP, Unspecified | Daicel PP |
| Diakon® ST35G8 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |