Nypol® PA A3 G30 HS UV RH PRTA011 NR393
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ifcAau_Nypol-PA-A3-G30-HS-UV-RH-PRTA011-NR393.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 in black color reinforced with 30% of fiberglass, heat stabilized, resistant ethylene glycol resistance to hydrolysis and UV. Good set of thermal properties, electrical and mechanical. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 to 1.38 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium, 50% RH) | 1.5 | -- | % | ASTM D570 |
| Relative Viscosity - Formic Acid | 46.0 to 52.0 | -- |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 230 | 150 | MPa | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 200 | 135 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.2 | 5.0 | % | ASTM D638 |
| Flexural Modulus | 12200 | 6500 | MPa | ASTM D790 |
| Flexural Strength | 210 | 190 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | 16 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | -- | 70 | kJ/m² | |
| 23°C | 70 | 85 | kJ/m² | |
| Notched Izod Impact (Area) | ASTM D256 | |||
| -30°C | 10.0 | 10.0 | kJ/m² | |
| 23°C | 11.0 | 14.0 | kJ/m² | |
| Unnotched Izod Impact (Area) (-30°C) | -- | 70.0 | kJ/m² | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | -- | 250 | °C | ASTM D648 |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | > 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+11 | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 36 | 29 | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.710 mm | -- | HB | ||
| 1.50 mm | -- | HB | ||
| 3.00 mm | -- | HB |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® N8860 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Sup-tech P280 | Shanghai Suptech Engineering Plastics Co. Ltd. | PP, Unspecified | Sup-tech |
| Chemlon® 130 G | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| ColorRx® TPE-OM70A0RXTL | LTL Color Compounders, Inc. | TPE | ColorRx® |
| E-Pos 327H | Epocat Nederland BV | Epoxy | E-Pos |