ACRYLITE® Sheet GP
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Cyro LLC |
| Trademark: | ACRYLITE® Sheet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ifRhTE_ACRYLITE-Sheet-GP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ACRYLITE® cell cast acrylic sheet is made to exacting standards. It offers excellent optical characteristics, thickness tolerances, light stability, and low internal stress levels for consistent performance. ACRYLITE® sheet is a lightweight, rigid thermoplastic material that has many times the breakage resistance of standard glass and is highly resistant to weather conditions. ACRYLITE® cell cast can be easily sawed, machined, thermoformed, and cemented and is ultraviolet light absorbing up to approximately 360 nanometers. Because of its unique properties, ACRYLITE® cell cast is ideal for a wide range of applications, such as:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 1(23°C) | 2.0 | % | ASTM D702 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 94 | ASTM D785 | |
| Barcol Hardness | 49 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2760 | MPa | ASTM D638 |
| Tensile Strength | 68.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.2 | % | ASTM D638 |
| Flexural Modulus | 3280 | MPa | ASTM D790 |
| Flexural Strength (Break) | 114 | MPa | ASTM D790 |
| Compressive Modulus | 2960 | MPa | ASTM D695 |
| Compressive Strength | 124 | MPa | ASTM D695 |
| Shear Strength | 62.1 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 21 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 98.9 | °C | ASTM D648 |
| Continuous Use Temperature | 82.2 | °C | |
| Vicat Softening Temperature | 115 | °C | ASTM D1525 |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat (25°C) | 1460 | J/kg/°C | |
| Thermal Conductivity | 0.19 | W/m/K | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.9E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.6E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 2(3.18 mm) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.50 | ASTM D150 | |
| 1 kHz | 3.20 | ASTM D150 | |
| 1 MHz | 2.70 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 0.060 | ASTM D150 | |
| 1 kHz | 0.040 | ASTM D150 | |
| 1 MHz | 0.020 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (3.00 mm) | 30 | mm/min | ASTM D635 |
| Self Ignition Temperature | 488 | °C | ASTM D1929 |
| Smoke density (3.00mm) | 11 | % | ASTM D2843 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Soluble Matter Loss | 0.0 | % | ASTM D570 |
| Weight Gain | ASTM D570 | ||
| During Immersion | 0.20 | % | ASTM D570 |
| During Immersion (14 days) | 0.060 | % | ASTM D570 |
| During Immersion (21 days) | 0.080 | % | ASTM D570 |
| During Immersion (35 days) | 1.0 | % | ASTM D570 |
| During Immersion (48 days) | 1.1 | % | ASTM D570 |
| During Immersion (7 days) | 0.050 | % | ASTM D570 |
| Forming Temperature | 171 - 193 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance | 92.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Absorption - Dimensional Change during Immersion, ASTM D570 : 0.2% |
| Note Message | |
|---|---|
| 1 . | Difference in length and width, before and after heating above 300°F |
| 2 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 685 FR HEC | RTP Company | ABS | RTP |
| Nypol® PA B3 G15 HL TZ PRTA010 NT333 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| APEX® 3701-75NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| DENISTAT P 30M21 03 SC1 | Vamp Tech | PP Copolymer | DENISTAT |
| Omnix® DW-4050 | Solvay Specialty Polymers | HPPA | Omnix® |