Styrolux® S
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Styrolux® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ifOuSP_Styrolux-S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Styrolux S is a new developmental, clear styrene-butadiene copolymer (SBC) designed specifically for blending with Styrolux T in order to enable high performance film extrusion and shrink film applications. As Styrolux S is blended with Styrolux T it increases the stiffness of the film and improves the storage stability of film reels (reduced natural shrinkage). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 11.0 | cm³/10min | ISO 1133 |
| Water Absorption (Saturation, 23°C) | 0.070 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore D | 74 | ASTM D2240 | |
| Shore D | 83 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 3240 | MPa | ASTM D638 |
| -- | 2900 | MPa | ISO 527-2 |
| Tensile Strength (Yield, 23°C) | 43.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.0 | % | ASTM D638, ISO 527-2 |
| Break, 23°C | 2.5 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2620 | MPa | ASTM D790 |
| -- | 3000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 68.3 | MPa | ASTM D790 |
| -- | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 11 | J/m | ASTM D256 |
| Unnotched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 71.7 | °C | ASTM D1525 1 |
| -- | 70.0 | °C | ISO 306/A50 |
| -- | 64.0 | °C | ISO 306/B50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (550 nm) | 91.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resirene READ 9400 RAF | Resirene, S.A. de C.V. | PS (HIPS) | Resirene |
| AKROMID® B3 GFM 10/20 1 L black (4679) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| Geon™ CPVC MC500 | PolyOne Corporation | CPVC | Geon™ CPVC |
| Infino CF-1030 | SAMSUNG SDI CO., LTD. | PC | Infino |
| Petrothene® LR590005 | LyondellBasell Industries | HDPE, HMW | Petrothene® |