Pro-fax 6331
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Pro-fax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ifBRyQ_Pro-fax-6331.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pro-fax 6331 general purpose polypropylene homopolymer is available in pellet form. This resin is typically used in injection molding applications. For regulatory compliance information see Pro-fax 6331 Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792B |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 34.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 11 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 2 | 1450 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 32 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 93.0 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M2101R (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Copolymer | Sanren |
| RheTech Polypropylene G30P100-00 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Tenopom® POM B3 G25 NTLA010 PR316 | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| Flontech® FT-900-D | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| KEBAFLEX® P D63.1 | BARLOG plastics GmbH | TPC-ET | KEBAFLEX® |