RTP ESD C 700 EG
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | idbUTq_RTP-ESD-C-700-EG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 2.5 - 3.5 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ASTM D638 |
| Tensile Strength | 27.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 1240 | MPa | ASTM D790 |
| Flexural Strength | 34.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact (18300 mm) | No Break | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Static Decay, FTMS101C 4046.1, MIL-PRF-81705D, 5kV to 50 V, 12% RH: <2 secSurface Resistance, ESD S11.11: < 1E5 ohmSurface Resistivity, ASTM D257: < 1E6 ohm/sqTensile Elongation, ASTM D638: >10%Volume Resistivity, ASTM D257: < 1E3 ohm-cmMelt Flow Rate, ASTM D1238, 190°C/2.16 kg: to 1 g/10 min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 193 - 232 | °C | |
| Mold Temperature | 21.1 - 65.6 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® 3540 | Wacker Chemie AG | Silicone | POWERSIL® |
| RTP 801 SI 2 | RTP Company | Acetal (POM) Copolymer | RTP |
| REXtac® APAO RT 1310 | Huntsman Corporation | PAO | REXtac® APAO |
| APEX® 77-W385-A | Teknor Apex Company | PVC, Flexible | APEX® |
| Sylvin 8980-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |