LGH 305
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | LG Polymers India Pvt. Ltd. |
| Trademark: | LGH |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | idGVrB_LGH-305.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LGSTRENE LGH 305 is a High Impact Polystyrene material. It is available in Asia Pacific. Primary attribute of LGSTRENE LGH 305: Flame Rated. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 93 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 23.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 1960 | MPa | ASTM D790 |
| Flexural Strength | 37.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 74 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 98.0 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-1934G | Teknor Apex Company | TES | Telcar® |
| Badamid® PA12 GK30 | Bada AG | Nylon 12 | Badamid® |
| AKROMID® S3 1 black (3317) | AKRO-PLASTIC GmbH | Nylon 610 | AKROMID® |
| Hostacom DKC745D | LyondellBasell Industries | TPO (POE) | Hostacom |
| KEBATER® PBT BF130 | BARLOG plastics GmbH | PBT | KEBATER® |