NILAMID® XS3 GF50/FA
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | Nilit Plastics |
| Trademark: | NILAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ibpLl6_NILAMIDXS3GF50FA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
SPECIALTY PARTIALLY AROMATIC POLYAMIDE BLEND
PARTIALLY AROMATIC PA, 50% GLASS FIBER REINFORCED, SUITABLE FOR FOOD CONTACT AND DRINKING WATER |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.58 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow : 23°C | 0.40 | -- | % | ISO 294-4 |
| Flow : 23°C | 0.080 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.60 | -- | % | ISO 62 |
| Saturated, 23°C | 4.2 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 17500 | 16500 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 240 | 210 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.8 | 3.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 11 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 13 | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 95 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 100 | 95 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 13 | 15 | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed) | 235 | -- | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 120 | -- | °C | IEC 60216 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 3 | 1.0E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+14 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 32 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.40 mm | HB | -- | UL 94 | |
| 0.8 mm | HB | -- | UL 94 | |
| 1.6 mm | HB | -- | UL 94 | |
| 3.2 mm | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | 2000 hr |
| 3 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 105 | RTP Company | PP, Unspecified | RTP |
| Sarlink® TPE ME-2259D BLK 288 | Teknor Apex Company | TPE | Sarlink® TPE |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 6221 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Bayflex® 110-50 (24% Mineral) | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| SCHULABLEND® (PA/PP) M/MO 5101 | A. Schulman Europe | Nylon+PP | SCHULABLEND® |