Polymer-E EV302
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Asia Polymer Corporation (APC) |
| Trademark: | Polymer-E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ibCnFo_Polymer-E-EV302.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polymer-E EV302 is an Ethylene Vinyl Acetate Copolymer (EVA) product. It can be processed by extrusion or foam processing and is available in Asia Pacific. Applications of Polymer-E EV302 include consumer goods and foam. Primary characteristic: good processability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 8.0 | wt% | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 44 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 14.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 680 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 46.0 | °C | ASTM D648 |
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 77.0 | °C | ASTM D1525 |
| Melting Temperature | 96.0 | °C | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Microthene® G MN71400 | LyondellBasell Industries | LDPE | Microthene® G |
| TEREZ PA 6.6 7500 TF 20 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| APEX® 3610-75 | Teknor Apex Company | PVC, Flexible | APEX® |
| APEX® 79-B427D-46 Black | Teknor Apex Company | PVC, Flexible | APEX® |
| DENISTAT M 00U 05 | Vamp Tech | Acetal (POM) Copolymer | DENISTAT |