LNP™ LUBRICOMP™ WFL33 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ib6IXS_LNP-LUBRICOMP-WFL33-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP WFL33 is a compound based on PBT containing 15% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound WFL-4033 Product reorder name: WFL33 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.53 | g/cm³ | ASTM D792 |
| -- | 1.52 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.70 to 0.90 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.050 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6360 | MPa | ASTM D638 |
| -- | 6200 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 90.0 | MPa | ISO 527-2/5 |
| Break 2 | 87.0 | MPa | ASTM D638 |
| Break | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 3.0 | % | ISO 527-2/5 |
| Break 3 | 2.9 | % | ASTM D638 |
| Break | 3.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 5700 | MPa | ASTM D790 |
| -- 5 | 5510 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 145 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 150 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 149 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.46 | ||
| vs. Itself - Static | 0.44 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 4.80 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 53.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 62 | J/m | ASTM D256 |
| 23°C 8 | 3.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 600 | J/m | ASTM D4812 |
| 23°C 9 | 38 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 7.50 | J | ASTM D3763 |
| -- | 1.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 222 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 221 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 207 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 196 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.4E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.2E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC P6180A | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Moplen HF600N | PolyMirae | PP Homopolymer | Moplen |
| Vistek 3030 | Visual Polymer Technologies, LLC | TP, Unspecified | Vistek |
| Nanjing Hongrui PBT T1000 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PBT | Nanjing Hongrui PBT |
| LEXAN™ HFD4471 resin | SABIC Innovative Plastics | PC | LEXAN™ |