ULTEM™ LTX300B resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ib5KyR_ULTEMLTX300Bresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Standard flow Polyetherimide blend with low toxicity, smoke, and flame evolution. ECO Compliant, UL94 V0 listing. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (295°C/6.6 kg) | 1.6 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.30 - 0.50 | % | Internal method |
| Transverse flow : 3.20mm | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3340 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 96.5 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 88 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 3210 | MPa | ASTM D790 |
| Flexural Strength 5 | ASTM D790 | ||
| Yield, 100mm span | 145 | MPa | ASTM D790 |
| Fracture, 100mm span | 141 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Reverse Notch Izod Impact (3.20 mm) | 2100 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 35.3 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 191 | °C | ASTM D648 |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 115 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 6 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.762 mm) | V-0 | UL 94 | |
| Halogen Content | 0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 310 - 332 | °C | |
| Middle Temperature | 321 - 343 | °C | |
| Front Temperature | 332 - 354 | °C | |
| Nozzle Temperature | 327 - 349 | °C | |
| Processing (Melt) Temp | 332 - 354 | °C | |
| Mold Temperature | 93.3 - 135 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN AX4000 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| RTP ESD C 201 | RTP Company | Nylon 66 | RTP |
| NYLOY® UB-0010N G50L1N | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| HiFill® PES GF30 | Techmer Engineered Solutions | PESU | HiFill® |
| Perlast® G70A | Precision Polymer Engineering Ltd. | Perfluoroelastomer | Perlast® |