LNP™ THERMOCOMP™ AF008 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ias1Pw_LNP-THERMOCOMP-AF008-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP AF008 is a compound based on Acrylonitrile Butadiene Styrene resin containing 40% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound AF-1008 Product reorder name: AF008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.20 to 0.40 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.18 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.22 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11300 | MPa | ASTM D638 |
| -- | 10200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 95.0 | MPa | ASTM D638 |
| Break 3 | 87.0 | MPa | ASTM D638 |
| Break | 85.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 4 | 1.4 | % | ASTM D638 |
| Break | 1.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 10700 | MPa | ASTM D790 |
| -- 6 | 10100 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 132 | MPa | ISO 178 |
| Break, 50.0 mm Span 7 | 136 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 72 | J/m | ASTM D256 |
| 23°C 8 | 7.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 300 | J/m | ASTM D4812 |
| 23°C 9 | 18 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 10.2 | J | ASTM D3763 |
| -- | 2.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 105 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 105 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 101 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 101 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 5.6E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Propionate 360A4000012 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Tenac™-C LT350 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| TRIREX® Compound 3025G20 | Samyang Corporation | PC | TRIREX® Compound |
| YUCLAIR® DX800 | SK Global Chemical | MDPE | YUCLAIR® |
| CAPROWAX P™ 6006-00-000 Granulat | POLYFEA | Biodeg Polymers | CAPROWAX P™ |