Lupolen 3026 K
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Lupolen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iahqCL_Lupolen-3026-K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupolen 3026 K is an additivated, low density polyethylene with high rigidity. It contains slip and anti-blocking agent. It is delivered in pellet form. Foodlaw compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.928 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 13.0 | MPa | ISO 527-2 |
| Coefficient of Friction (Blown Film) | < 0.20 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 0.6-1.6 mil (15-40 µ) | ||
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm, blown film | 20.0 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 15.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 300 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 550 | % | ISO 527-3 |
| Dart Drop Impact (50 µm, Blown Film) | 90 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 97.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 114 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20, 50.0 µm, blown film | > 70 | ASTM D2457 | |
| 60, 50.0 µm, blown film | > 110 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | < 8.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Erucamide | 0.070 | % | DIN 51454 |
| Failure Energy (50.0 µm) | 35.0 | J/cm | DIN 53373 |
| Natural Silica | 0.10 | % | ISO 3451-1 |
| Melt temperature- Film | 150 - 190 | °C | |
| Film properties tested using 50 µm thickness blown film extruded at a melt temperature of 170°C and a blow-up ratio of 2:1. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer N70J | Precision Polymer Engineering Ltd. | NBR | Precision Polymer |
| TORZEN® G3300HSL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Ultramid® 8202C HS | BASF Corporation | Nylon 6 | Ultramid® |
| Colorite 88 Series 8088 | Colorite Polymers | PVC, Unspecified | Colorite 88 Series |
| CP PRYME® Polypropylene PPC100ZNA/3.5I-12M NAT | Chase Plastics Services Inc. | PP Impact Copolymer | CP PRYME® Polypropylene |