Ultramid® B3ZG6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iae5fA_Ultramid-B3ZG6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3ZG6 is an impact-modified, 30% glass fiber reinforced injection molding PA6 grade for industrial items having very high impact strength and rigidity. Applications Typical applications include automotive airbag housings and half-shells for suitcases. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.33 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 25.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | -- | % | |
| Water Absorption | ||||
| Saturation | 6.2 | -- | % | ASTM D570 |
| Saturation, 23°C | 6.2 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.0 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9000 | 5300 | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Break, 23°C | 138 | -- | MPa | ASTM D638 |
| Break, 23°C | 150 | 100 | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Break, 23°C | 3.6 | -- | % | ASTM D638 |
| Break, 23°C | 3.6 | 10 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 7860 | -- | MPa | ASTM D790 |
| 23°C | 7400 | 4700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 220 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 15 | -- | kJ/m² | |
| 23°C | 20 | 35 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 90 | -- | kJ/m² | |
| 23°C | 95 | 110 | kJ/m² | |
| Notched Izod Impact | ||||
| -40°C | 140 | -- | J/m | ASTM D256 |
| 23°C | 190 | -- | J/m | ASTM D256 |
| -30°C | 10 | -- | kJ/m² | ISO 180 |
| 23°C | 20 | 32 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 207 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE | ||||
| Flow | 1.0E-5 | -- | cm/cm/°C | ASTM E831 |
| Flow | 2.3E-5 | -- | cm/cm/°C | |
| Transverse | 6.5E-5 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.730 mm | 150 | -- | °C | |
| 1.50 mm | 150 | -- | °C | |
| 3.00 mm | 150 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.730 mm | 115 | -- | °C | |
| 1.50 mm | 115 | -- | °C | |
| 3.00 mm | 120 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.730 mm | 150 | -- | °C | |
| 1.50 mm | 150 | -- | °C | |
| 3.00 mm | 150 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | 1.0E+13 | 1.0E+10 | ohms·cm | ASTM D257 |
| -- | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.80 | 6.80 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.20 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.730 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Rear Temperature | 245 to 275 | °C | |
| Middle Temperature | 260 to 285 | °C | |
| Front Temperature | 270 to 295 | °C | |
| Nozzle Temperature | 270 to 295 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SINOF P140T-04 | SINOF HI-TECH MATERIAL CO. LTD | PPS | SINOF |
| Moplen HP500M | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| TAROLOX 111 G6 Y0 | Taro Plast S.p.A. | PET | TAROLOX |
| TOTAL Polypropylene PPH 3862 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Chemlon® 225 GVNH BK555 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |