Resilience™ LS21000E
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Resilience™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ia9ubn_ResilienceLS21000E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Resilience™LS21000E is a rigid polyvinyl chloride product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: lighting equipment. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 13254 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 77 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2820 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 44.8 | MPa | ASTM D638 |
| Flexural Modulus | 3150 | MPa | ASTM D790 |
| Flexural Strength | 80.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C, 3.18 mm, Compression Molded) | 190 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 4 | 89.4 | J/cm | ASTM D4226 |
| 23°C 5 | > 138 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, annealed, 3.18mm 6 | 77.5 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm 7 | 75.6 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm, molded 8 | 72.7 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm, molded 9 | 75.3 | °C | ASTM D648 |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.9 mm, ALL) | V-0 | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ease of Sizing | Excellent | ||
| Physical property tests based on white 1185 lot#15141264 box 1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Test specimens prepared from compression molded milled sheet. |
| 4 . | Procedure A, C.125 Throwing |
| 5 . | Procedure B, C.125 Throwing |
| 6 . | Test specimens annealed at 60 deg.C |
| 7 . | Test specimens annealed at 50 deg.C |
| 8 . | Test specimens annealed at 50 deg.C |
| 9 . | Test specimens annealed at 60 deg.C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE M80063 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Sinpolene MBW3191 | Teknor Apex Asia Pacific PTE. LTD. | LLDPE | Sinpolene |
| TEKAMID™ HG20L | Mando Advanced Materials Co., Ltd. | ABS+Nylon | TEKAMID™ |
| WONDERLITE® PC-122U | CHI MEI CORPORATION | PC | WONDERLITE® |
| SABIC® PPcompound 7705 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |