Braskem PE GM5240PR
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iZQExq_Braskem-PE-GM5240PR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GM5240PR is a High Density Polyethylene compound specially developed for the manufacturing of pipes, underground conduits, and steel pipe coating. This resin is produced with bimodal technology and shows excellent mechanical properties and resistance to stress cracking. GM5240PR contains carbon black pigment that protects it against ultraviolet radiation action and photodegradation. Application: Triple-layer coating for metallic pipes; localized irrigation pipes; ducts for mining. Process: Extrusion |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.957 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.55 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (2.00 mm, 100% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693 |
| Carbon Black Content | 2.4 | % | ASTM D1603 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 61 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 23.0 | MPa | |
| Break, Compression Molded | 28.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, Compression Molded | 9.9 | % | |
| Break, Compression Molded | 840 | % | |
| Flexural Modulus - 1% Secant (Compression Molded) | 980 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 68.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 121 | °C | ASTM D1525 1 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| UV Absorption Coefficient | > 3000 | Abs/cm | ASTM D3349 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8200-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Braskem PP RP 250 | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| Fainplast PVC GS 55/AT | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| KumhoSunny PC/PET KCA9361 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+PET | KumhoSunny PC/PET |
| Ipethene® 810 | Carmel Olefins Ltd. | LDPE | Ipethene® |