SABIC® Vestolen A 6012
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® Vestolen A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iZA7AI_SABIC-Vestolen-A-6012.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC®Vestolen A 6012 is a high-density polyethylene product,. It can be processed by extrusion or fiber (spinning) extrusion and is available in Europe. SABIC®Vestolen A 6012 applications include textile/fiber, glue/gummed paper and food contact applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.90 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 2.8 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec, Compression Molded) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1200 | MPa | ISO 527-2/1BA/1 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 27.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | 40.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | 2000 | % | ISO 527-2/1BA/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 18 | kJ/m² | ISO 180/1A |
| 23°C | 27 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 79.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 45.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 128 | °C | ISO 306/A50 |
| -- | 72.0 | °C | ISO 306/B50 |
| Additional Information |
|---|
| Strain at Break, ISO 527, Compression Molded, Type 1BA, 50mm/min, 2mm: >2000%ESCR, SABIC Method, Compression Molded, Determined in Rhodacal-DS10 at 75°C, 3 N/mm², thickness 1mm: 100hrMelting Point, DIN 53765, Tmelt(top) at 5°C/min: 134°CEnthalpy Change, DIN 53765: 215J/g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE PCG80063 | SABIC Americas, Inc. | HDPE | SABIC® HDPE |
| TechnoFin 1355 | TechnoCompound GmbH | PP, Unspecified | TechnoFin |
| TITANZEX® HI1100 | Lotte Chemical Titan (M) Sdn. Bhd. | HDPE | TITANZEX® |
| Flontech® FT-GR15-3 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| LNP™ LUBRILOY™ Lexan_WR6300 compound | SABIC Innovative Plastics | AES+PC+SAN | LNP™ LUBRILOY™ |