RTP 4002 TFE 15
| Category: | PPA , Polyphthalamide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iYygEC_RTP-4002-TFE-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.24 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8270 | MPa | ASTM D638 |
| Tensile Strength | 114 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.4 | % | ASTM D638 |
| Flexural Modulus | 6550 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 232 | °C | ASTM D648 |
| CLTE - Flow | 3.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D955, 0.25in.: 6mil/in. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 304 - 332 | °C | |
| Middle Temperature | 304 - 332 | °C | |
| Front Temperature | 304 - 332 | °C | |
| Mold Temperature | 93.3 - 163 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® E 70 G | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| XANTAR® G6F 23 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| ALPHALAC SF510 | LG Chem Ltd. | PS (HIPS) | ALPHALAC |
| CROSSVINIL ME/85 PA | Crosspolimeri S.p.A. | PVC, Unspecified | CROSSVINIL |
| PELPRENE™ S6002 | TOYOBO America, Inc. | TPEE | PELPRENE™ |