Bayfill® NV 100
| Category: | PUR-Ether/MDI , Polyurethane (Polyether, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Bayfill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iVq5qF_Bayfill-NV-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bayfill NV 100 acoustic cavity-filling foam is a two-component polyurethane system designed to fill and acoustically seal cavities of automobile body shells. The Bayfill NV 100 acoustic cavity-filling foam system can be processed on both high- and low-pressure equipment. It is poured at a 1:1 ratio, providing excellent mix even on low-pressure equipment and an excellent shot-to-shot repeatability. Comparable low concentrations of residual MDI and low foam surface temperatures allow for safer dispense operations. As with any product, use of the Bayfill NV 100 acoustic cavity-filling foam system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. The Bayfill NV 100 acoustic cavity-filling foam system is supplied as two components. Component A is a modified polymeric diphenylmethane diisocyanate blend. Component B is a polyether polyol system. |
| General Information | |
|---|---|
| Uses |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength (10% Strain) | 0.0269 | MPa | ASTM D1621 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 71 | mm/min | FMVSS 302 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mix Ratio by Weight: 1.0, Mix Ratio by Volume: 1.0 | ||
| Component B | Mixing ratio by weight: 1.0, mixing ratio by capacity: 1.2 | ||
| Shelf Life (25°C) | 26 | wk |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dimensional Stability, Volume Change | MSCD 643 | ||
| 38°C 1 | -3.5 | % | MSCD 643 |
| 120°C 2 | -0.060 | % | MSCD 643 |
| 24 hr : 120°C | -1.7 | % | MSCD 643 |
| Dimensional Stability, Weight Change 3 | 0.91 | % | MSCD 643 |
| Dispensed Weight Loss | % | MSCD 643 | |
| Heat Aged Weight Loss - 24 hr (80°C) | % | MSCD 643 | |
| Part A Type: Isocyanate Appearance: Dark brown to black liquid Specific Gravity @ 25°C: 1.24 Viscosity @25°C: 700 mPa-s Flash Point PMCC: 213°C Part B Type: Polyol Appearance: Opaque white liquid Specific Gravity @ 25°C: 1.04 Viscosity @25°C: 2050 mPa-s Flash Point PMCC: 115°C Material Temperature: 140°FMachine Reactivity at 35°C Gel Time: <3 sec Rise Time: <6 sec Tack-Free Time: <9 sec Free-Rise Density: 1.6 lb/ft³ Foam Surface Exotherm: <58°CFoam Core Exotherm: <110°CVolumetric Expansion: 4500% |
| Note Message | |
|---|---|
| 1 . | 168 hr, 100% RH |
| 2 . | 15 min, 20 min after foaming |
| 3 . | during humid aged test |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1387 TFE 15 | RTP Company | PPS | RTP |
| RTP VLF 84707 | RTP Company | PTT | RTP |
| Ecotan B F30 R NERO | Soredi S.p.a. | Nylon 6 | Ecotan B |
| Hanwha Total PE E210F | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | EVA | Hanwha Total PE |
| LNP™ VERTON™ MV008SU compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |