| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Cevian®-N |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iV0Bvg_Cevian--N-050-050SF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cevian®-N 050, 050SF is a Styrene Acrylonitrile (SAN) material. It is available in Asia Pacific. Primary attribute of Cevian®-N 050, 050SF: Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 32 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 70.0 | MPa | ISO 527-2 |
| Flexural Modulus | 3600 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 6.40 mm) | 20 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 12.7 mm | 94.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 83.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Ball Pressure Test | 90 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.50 mm) | 35 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 170 to 190 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 210 to 230 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 10.0 to 20.0 | MPa | |
| Screw Speed | 70 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STERLENE™ BMU147E | R&P (Pte.) Ltd. | TPO (POE) | STERLENE™ |
| DILAMID® 6 FVT 30 BLACK | Dilaplast S.p.A. | Nylon 6 | DILAMID® |
| FRAGOM XLC/125 R | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| LNP™ STAT-KON™ OX00428 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ STAT-KON™ |
| LNP™ THERMOCOMP™ JF004 compound | SABIC Innovative Plastics | PESU | LNP™ THERMOCOMP™ |