LNP™ LUBRICOMP™ HFG25Z compound
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iUaog3_LNPLUBRICOMPHFG25Zcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP HFG25Z is a compound based on Nylon 11 resin containing Glass Fiber, Graphite Powder. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound HFL-4325 Product reorder name: HFG25Z |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.47 | % | Internal method |
| Flow : 24 hours | 0.40 - 0.60 | % | ASTM D955 |
| Transverse flow | 0.93 | % | Internal method |
| Transverse flow : 24 hours | 0.80 - 1.0 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.93 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.47 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11000 | MPa | ASTM D638 |
| -- | 6830 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 152 | MPa | ASTM D638 |
| Yield 2 | 153 | MPa | ASTM D638 |
| Yield | 76.0 | MPa | ISO 527-2, ISO 527-2/5 |
| Fracture | 152 | MPa | ASTM D638 |
| Fracture 3 | 153 | MPa | ASTM D638 |
| Fracture | 76.0 | MPa | ISO 527-2, ISO 527-2/5 |
| Tensile Elongation | |||
| Yield | 2.7 | % | ASTM D638 |
| Yield 4 | 2.8 | % | ASTM D638 |
| Yield | 2.3 | % | ISO 527-2, ISO 527-2/5 |
| Fracture | 2.7 | % | ASTM D638 |
| Fracture 5 | 2.8 | % | ASTM D638 |
| Fracture | 2.4 | % | ISO 527-2, ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 5520 | MPa | ASTM D790 |
| -- | 5520 | MPa | ASTM D790 |
| -- | 18200 | MPa | ISO 178 |
| -- 7 | 18200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 96.5 | MPa | ASTM D790 |
| -- | 352 | MPa | ISO 178 |
| -- | 352 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 98.0 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.42 | ASTM D3702 Modified | |
| With Self-Static | 0.46 | ASTM D3702 Modified | |
| Wear Factor - Washer | 58.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 69 | J/m | ASTM D256 |
| 23°C 9 | 7.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 450 | J/m | ASTM D4812 |
| 23°C 10 | 29 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 15.1 | J | ASTM D3763 |
| -- | 3.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 182 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 11 | 182 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 171 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 166 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 9.2E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flow : 23 to 60°C | 9.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 3.4E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 232 - 243 | °C | |
| Front Temperature | 260 - 271 | °C | |
| Processing (Melt) Temp | 227 - 260 | °C | |
| Mold Temperature | 43.3 - 54.4 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® 70G30L NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Capilene® T 77 A | Carmel Olefins Ltd. | PP Homopolymer | Capilene® |
| Colorite G Series 4012G-015 | Colorite Polymers | PVC, Flexible | Colorite G Series |
| MAJORIS BG305 | AD majoris | PP, Unspecified | MAJORIS |
| Sylvin 9067-80 YELLOW 495 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |