| VA-286 is a tough, heat-resistant polyurethane formulated for vacuum assisted casting systems and short mold cycle times. Excellent physical properties can be obtained without the utilization of mercury, MOCA, or TDI. VA-286 has a longer gel time than VA-285, allowing for larger castings. VA-286 can be easily pigmented. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.13 | g/cm³ | |
| Cured | 1.20 | g/cm³ | |
| Base Resin | 1.25 | g/cm³ | |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2520 | MPa | ASTM D790 |
| Flexural Strength | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 95.0 | °C | |
| 1.8 MPa, Unannealed | 84.0 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 60 Mix Ratio by Weight: 54 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 45 to 75 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 38°C 1 | 0.20 | Pa·s | |
| 38°C 2 | 0.50 | Pa·s | |
| 38°C 3 | 0.97 | Pa·s | |
| Curing Time 4 | 25 | hr | |
| Gel Time | 7.0 to 11 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 80 to 90 | ASTM D2240 | |
| Tensile Strength | 68.9 | MPa | ASTM D638 |
| Tensile Elongation at Break | 5.0 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 24 hours at 77°F + 1 hour at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex SD-0170 F | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Bayblend® W85 HI | Covestro - Polycarbonates | ASA+PC | Bayblend® |
| Clariant Nylon 6/6 6608M33-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| GAPEX® FPP30GQ11HB | Ferro Corporation | PP, Unspecified | GAPEX® |
| Karina IVORY PVC COMPOUND -E 830-35/ 1-Y-ERYB-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |