RTP ESD A 400 HI
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iSIKVH_RTP-ESD-A-400-HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2410 | MPa | ASTM D638 |
| Tensile Strength | 19.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 7.0 | % | ASTM D638 |
| Flexural Modulus | 2210 | MPa | ASTM D790 |
| Flexural Strength | 37.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 96.1 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 79.4 | °C | ASTM D648 |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D955, 0.25in.: 8mil/in.Tensile Elongation, ASTM D638: 7-10%Volume Resistivity, ASTM D257: 10E3-10E9 ohm-cmSurface Resistivity, ASTM D257: 10E6-10E12 ohm-cmStatic Decay, FTMS-4046.1, Mil B-81705C: <2.0 seconds |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 204 - 288 | °C | |
| Middle Temperature | 204 - 288 | °C | |
| Front Temperature | 204 - 288 | °C | |
| Mold Temperature | 37.8 - 71.1 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTOUGH PZ726 | Polyram Ram-On Industries | PC | RAMTOUGH |
| Mirakutoran® TPU E675MNAT | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Wellamid® XT1627-BK2 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Eco-Solutions GP315-1 | MINIMA Technoloy Co. Ltd. | Biodeg Polymers | Eco-Solutions |
| REV Materials 8009-003 | REV Materials | PP, Unspecified | REV Materials |