AXELERON™ FO 6318 BK CPD
| Category: | HDPE , Black High Density Polyethylene Compound for Cable Jacketing |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AXELERON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iRcacK_AXELERON-FO-6318-BK-CPD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High density cable sheath material AXELERON™FO A- 6318 BK is a kind of UNIPOL™High density polyethylene sheath material prepared by PE process. This material is easy to process, has small shrinkage, and has a good balance in toughness, stress cracking resistance, wear resistance and weather resistance. AXELERON™FO A- 6318 BK is suitable as a sheath material for optical cable cables. Specifications AXELERON™FO A- 6318 BK meets the following raw material specifications:
Under the conditions of adopting the correct commercial extruder extrusion processing specifications, use AXELERON™The wires and cables of FO A- 6318 BK as sheath material shall meet the following specifications:
|
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.954 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal, F0) | > 450 | hr | ASTM D1693 |
| Carbon Black Content | 2.6 | % | ASTM D1603 |
| Absorption Coefficient - (kAB/m) | > 400 | ASTM D3349 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat resistant stress crack- F0 | > 336 | hr | ASTM D2951 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 22.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 600 | % | ASTM D638 |
| Flexural Modulus | 896 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow (23°C) | 1.3E-4 | cm/cm/°C | Internal method |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 2.50 | ASTM D1531 | |
| Dissipation Factor (1 MHz) | 3.0E-4 | ASTM D1531 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 218 - 260 | °C |
| Extrusion instructions |
|---|
| AXELERON™ FO 6318 BK CPD Jacket Compound can be processed in a wide range of extrusion equipment using flat profiles of 425-500°F (218-260°C). Hopper drying at 175°F (80°C) to remove moisture is recommended. However, specific recommendations for processing conditions can be determined only when the application and type of processing equipment are known. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1381 TFE 10 | RTP Company | PPS | RTP |
| Santoprene™ 8223-30M300 | ExxonMobil Chemical | TPV | Santoprene™ |
| Shandong PA1212 PA1212C-02 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| Witcom PA66 6LC-EM-HS | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| Sylvin 2986-60 White 1577 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |