InnoTuf® HP-2160A
| Category: | TSU-Ether , Polyurethane Thermoset Elastomer, Polyether Based |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTuf® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iRCqKV_InnoTuf-HP-2160A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HP-2160A is a high performance polyether based polyurethane elastomer formulated for hand-batch processing methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or MDI. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 0.990 | g/cm³ | |
| Cured | 1.02 | g/cm³ | |
| Base Resin | 1.08 | g/cm³ | |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 46 Mix Ratio by Weight: 43 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time (66°C) | 180 to 300 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.34 | Pa·s | |
| 25°C 2 | 1.7 | Pa·s | |
| 25°C 3 | 3.6 | Pa·s | |
| Curing Time 4 | 29 | hr | |
| Gel Time | 10 to 20 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 55 to 65 | ASTM D2240 | |
| Tensile Strength | 6.21 | MPa | ASTM D638 |
| Tensile Elongation at Break | 150 | % | ASTM D638 |
| Tear Strength | 22.8 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 5 hours at 150°F + 24 hours at 77°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong Aobang TPU-Polyester 64-D | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyester | Shandong Aobang TPU-Polyester |
| Taitarex® 866NM / BM | Taita Chemical Company, Ltd. | PS (GPPS) | Taitarex® |
| NEALID XG370 | AD majoris | Nylon+Olefin | NEALID |
| Geon™ Vinyl Wire & Cable WEMB410B | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| Plenco 03303 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |